Surface Treatment : Black Oxidized, Plain Oiled, Color Painting, Zinc, HDG, or according to customers' requirement.
Raw Material: 60Si2MnA, 60Si2CrA, 55Si2Mn, 38Si7
Hardness: 44-48HRC
Standard: DIN17221, BS970, GB/T1222
Fatigue life: 5 Million Times without Crack
Partnership: Agents, Distributors are welcome
Quality Control: Inspection on each workshift/new batch material/machine adjustment
Diameter: 14mm
Weight: 0.5KG
Type: GL1419 Rail Clip
GL Rail Clips for South American Railway Fastening System
Our rail clips range from 12mm to 20mm, such as e1809,e2009,e2055, skl1,skl3,skl12,skl14. The hardness is HRC42-47. Our rail clips are produced with standards DIN17221,BS970,GB/T4357,GB/T4358. On the fatigue life, when the deflection is 9.1mm,they can provide a performance of 5 million cyles without crack.
Item Name | Gl1409 Railway Gauge Lock Clip | |||
Type | E clip (e1809, e2006,e2007,e2009,etc) | |||
Skl clip (skl1,skl3,skl12,skl14) | ||||
Or the type by customers' drawings | ||||
Material | 60Si2MnA | 60Si2CrA | 55Si2Mn | 38Si7 |
Chemical composition(%) | C:0.56-0.64, Mn:0.60-0.90, Si:1.60-2.00, Cr:≤0.35, P:≤0.03, S:≤0.03 | C:0.56-0.64, Mn:0.40-0.70, Si:1.40-1.80,Cr:0.70-1.00 P:≤0.03, S:≤0.03 | C:0.52-0.60, Mn:0.60-0.90, Si:1.50-2.00,Cr:≤0.35 P:≤0.03, S:≤0.03 | C:0.35-0.42, Mn:0.50-0.80, Si:1.50-1.80, P:≤0.03, S:≤0.03 |
Hardness | For e clip: 44-48HRC For skl clip: 42-47HRC |
|||
Fatigue life | for Dia.18 is 3 millions cycles without breaking for Dia.20 is 5 millions cycles without breaking |
|||
Surface | plain (oiled), Oxide black, color painting, HDG, Zinc Plating... | |||
Standard refers | DIN17221, BS970, GB/T1222 |