E1809, E1817, E2055, E2009 Rail Clip Fastening System
E Type Rail Clip for Railway Track used with railway sleeper to fasten rails on both sides. The rail clips are usually made of forged spring steel, which are manufactured by hot forging process. The forged rail clips are considered to be better than other metal forming process due to most uniform microstructure.
| Name | Clip-E2055 Railway Fasteners System for Subway | |||
| Material | 60Si2MnA | 60Si2CrA | 55Si2Mn | 38Si7 |
| Chemical composition(%) | C:0.56-0.64, Mn:0.60-0.90, Si:1.60-2.00, Cr:≤0.35, P:≤0.03, S:≤0.03 | C:0.56-0.64, Mn:0.40-0.70, Si:1.40-1.80,Cr:0.70-1.00 P:≤0.03, S:≤0.03 | C:0.52-0.60, Mn:0.60-0.90, Si:1.50-2.00,Cr:≤0.35 P:≤0.03, S:≤0.03 | C:0.35-0.42, Mn:0.50-0.80, Si:1.50-1.80, P:≤0.03, S:≤0.03 |
| Hardness | HRC 42-47 | |||
| Fatigue life | 5 millions cycles without breaking | |||
| Surface | Plain (oiled), Oxide black, color painting | |||
| Standard refers | GB/T 1222,DIN 17221 | |||
Material: Spring steel
1.60Si2MnA
2.60Si2CrA
3.55Si2Mn
4.38Si7Our Elastic rail clips range from 12mm to 20mm, such as e1809,e2009,e2055, skl1,skl3,skl12,skl14. The hardness is HRC42-47. Our rail clips are produced with standards DIN17221,BS970,GB/T4357,GB/T4358.
On the fatigue life, when the deflection is 9.1mm,they can provide a performance of 5 million cyles without crack.
| Item Name | Elastic Rail Clip | |||
| Type | E clip (e1809, e2006,e2007,e2009,etc) | |||
| Skl clip (skl1,skl3,skl12,skl14) | ||||
| Or the type by customers' drawings | ||||
| Material | 60Si2MnA | 60Si2CrA | 55Si2Mn | 38Si7 |
| Chemical composition(%) | C:0.56-0.64, Mn:0.60-0.90, Si:1.60-2.00, Cr:≤0.35, P:≤0.03, S:≤0.03 | C:0.56-0.64, Mn:0.40-0.70, Si:1.40-1.80,Cr:0.70-1.00 P:≤0.03, S:≤0.03 | C:0.52-0.60, Mn:0.60-0.90, Si:1.50-2.00,Cr:≤0.35 P:≤0.03, S:≤0.03 | C:0.35-0.42, Mn:0.50-0.80, Si:1.50-1.80, P:≤0.03, S:≤0.03 |
| Hardness | For e clip: 44-48HRC For skl clip: 42-47HRC |
|||
| Fatigue life | for Dia.18 is 3 millions cycles without breaking for Dia.20 is 5 millions cycles without breaking |
|||
| Surface | plain (oiled), Oxide black, color painting, HDG, Zinc Plating... | |||
| Standard refers | DIN17221, BS970, GB/T1222 |
|||